Microstructural and dielectric responses of calcium copper titanate added soda-lime glass for high frequency devices

Abstract

The microstructures and dielectric responses of calcium copper titanate (CCTO) ceramics with soda-lime glass addition was investigated. The addition of soda lime glass was varied from 0-5 wt.% by solid-state reaction. The dielectric properties of CCTO indicated that dielectric constant was increased while dielectric loss was decreased after glass addition. The SEM micrographs showed the grain size of CCTO was decreased while the grain boundaries area of CuO + glass were increased after the addition of soda-lime glass. Both XRD patterns of CCTO and CCTO-soda lime glass sintered samples showed the formation of CCTO phase with minor peaks of CuO phase, respectively. These results indicated that soda-lime glass addition gave a significant effect on the microstructural and dielectric responses of CCTO ceramics.